    Performance test                  From the test rport issued by INTERTEK according to ASTM standard
    Clause Requirement-Test Result-Remark Verdict
    Hardness ASTM D1037-06a,Clause17    The modified Janka-ball test method shall be used with a "ball" 0.444in.in diameter.The load shall be recorded when the “ball”has penetrated to one-half its diameter into the panel.                                            The load shall be applied continuously throughout the test at a uniform rate of motion of the movable crosshead is 0.25 inch/minute. Combined four single pieces (single thickness 6 mm) together;Place the ball on top surface;              Average maximum load:7166N, with rack. No Verdict
             Impact             resistance ASTM D256-06a       Used 2.75J pendulum type hammers, mounted in lzod-type machine, in breaking standard specimens with one pendulum swing. Six standard specimens perpared in accordance with section 7.2; Sample width: 12.7mm; Sample depth under notch:10.6mm;           Test method: method C;

    Failure categories: C completed break;       Average notch impact risistance:22.8J/m;

    Average estimated toss correction:0.16J: Net impact resistance :10.2J/m

    No Verdict
    Bulk Density ASTM D6111-03      The weight of sample in air:4.81g; Overall weight of totally immersed sinker , cage, and partially immersed wire:184.23g: Overall weight of specimen completely immersed and of the wire partially immersed in liquid:182.27g; Average density:D23c=1.39g/m³ No Verdict
    Coefficient of Themal Expansion ASTM E228-06      ℃ to 50℃; The original length:50.56mmTemperature from 20 Average: 1.14×10-5 m/m. No Verdict
    Tensile Properties  ASTM E638-03      The thickness at the center of sample is 4mm; And the width at the center of sample is 6mm.The specimen is perpared in Type IV accordance with Section 6. The speed of testing is 5mm/minute. The tensile strength at break is reported. Average Tensile Strength at Break:21.6MPa No Verdict
            Flexural              Properties ASTM D790-07       The depth of samples is 5.79mm. The width of sample is 24.32mm. The default radii of loading nose and support are (5.0±0.1)mm. The test utilizes the three-point loading system and the support span-to-depth ratio is 16:1 The rate of crosshead motion is calculated in accordance by Equation 1, Sectoin 10.1.4. The flexural stress at break is reported. Average flexural stress at break is 38.2 Mpa No Verdict
     RoHS Requirement

    2002/95/EC AND AMMENDMENT 2005/618/EC                                                     Limits Content of Cadmium (Cd) is 100ppm;                                                          Limits Content of Lead (Pb) is 1000ppm;                                                               Limit Content of Mercury (Hg) is 1000ppm;                                                         Limits Content of Chromium (VI) (Cr6+) is 1000ppm;                                             

    Limits Content of Polybrominated Biphenyls (PBBs) is 1000ppm;                       

    Limits Content of Polybromianted Diphenyl Ethers (PBDEs) is 1000ppm.

    Cadmium (Cd)content ND,               

     Reporting Limit is 2ppm;                        

    Lead Content (Pb) is 85ppm;           

    Reporting Limit is 2ppm;                      Content of Mercury (Hg) is ND Reporting Limit is 2ppm;                           Chromium (VI)(Cr6+) Content is ND Reporting Limit is 1ppm;              Polybrominated Biphenyls (PBBs) Content is ND                              Reporting Limit is 5ppm;     Polybrominated Diphenyl Ethers (PBDEs) Content is 52ppm,                      Reporting Limit is 5ppm.

    Remark:ppm= Parts per      Millon=mg/kg        ND=Not Detected